Description
Creamy -Soft
consistency
Suitable for Vertical surface application
Very good adhesionon stone
Fast Hardening (20-60 minutes)
Good WorkingProperties (Polishing, Grinding, Milling& Drilling)
Low shrinkage
Water ,Petrol & Mineral oil resistance
Good heat resistance (70-80
Find the Right Size for Every Application
Tubes
Find the Right Size for Every Application
Metal Tin
1.5kg set
Lorem ipsum dolor sit amet, consectetur adipiscing elit. Ut elit tellus, luctus nec ullamcorper mattis, pulvinar dapibus leo.
Technical Specifications
| COMPONENT | Solid Mastic | Liquid Mastic |
|---|---|---|
| Viscosity cps 25°C 20 r.p.m. (ASTM D2196) | Tixotropic paste | 15000-19000 cps |
| Density at 25°C gr/cm' | 1.8-1.9 | 1.7 |
| Aspect | Coloured paste | Coloured liquid |
| Ratio of use glue/hardener | 100+2/3 | 100+2/3 |
| Gel time (in bulk) at 25°C in min | 4-5 | 3-4 |
| Tacky free in thin layer at 25°C in min | 25-30 | 15-20 |
| Working time suggested at 25°C in min | 60-80 | 60-80 |
| Minimum reaction temperature | 0°C | 0°C |
| Minimum temperature of use after hardening | 0°C | 0°C |
| Maximum temperature of use after hardening | +100°C | +100°C |
| Shelf life at 18-25°c | 12 months | 6 months |
| Ultimate tensile stress MPa | 50 | 50 |
| Extensibility | >2% | >2% |
| Tensile modulus | 4000 | 4000 |
| Breaking load Mpa | 110 | 110 |
| Adhesion force at 25°C marble botticino polished after 2 hours | 4.0 | 4.0 |
| Adhesion force at 25°C marble botticino polished after 2 hour | 5.4 | 5.5 |
How to Apply
The surfaces to be bonded should be thoroughly cleaned & dried. •Before adding the hardener, the Resin base can be tinted with colour paste to match the colour of the stone if required.
Dispense the required amount of Resin base from the tin & mix thoroughly with the necessary Hardener paste 3% by weight, to prepare the mixture ready for application.
Do not return the unused mixture back in the tin. • Keep the tins tightly closed after usage. •Store the tin & hardener in a cool place away from sunlight. •DOSAGE: 100 parts of Resin base + 3% parts of Hardener. GEL TIME: 3-10 minutes at 25° C (77° F). The Gel (working) time is reduced by heat & increased by cold
Brand Name Registerted